Surface characteristics of titanium-silver alloys in artificial saliva

H. M. Shim, K. T. Oh, J. Y. Woo, C. J. Hwang, K. N. Kim

Research output: Contribution to journalArticlepeer-review

10 Citations (Scopus)


Titanium and its alloys are widely used in biomedical and dental fields because of their excellent corrosion resistance and biocompatibility. It is well known that titanium is protected from corrosion because of the stability of the passive film that controls and determines the corrosion resistance and biocompatibility of titanium and its alloys. The purpose of this study was to evaluate the electrochemical properties of titanium-silver alloys and the surface characteristics of passive film in artificial saliva. We designed titanium-silver alloys with silver contents ranging from 0 to 5 at.%, in 1% increments. These alloys were arc-melted, homogenized, hot-rolled to 2 mm thickness, and finally solution heat-treated for 1 h and quenched. Potentiostatic testing was performed, and the open circuit potentials of the alloys were measured in artificial saliva, at 37°C. The passive films of the titanium-silver alloys were analyzed via XPS. Titanium-silver alloys maintained low current density and showed stable passive region and also had high open circuit potential as compared with pure titanium. The open circuit potential of titanium-silver alloys increased as silver addition increased. With regard to the fraction of oxygen species, a component of over 80% was found to be comprised of oxide. Therefore, the titanium surface mainly consisted of titanium oxide and, on the titanium-silver alloys, this film was composed of TiO2, Ti2O3, and TiO. As silver content increased, the TiO2 fraction also increased, as did the thickness of the titanium oxide layer formed.

Original languageEnglish
Pages (from-to)25-31
Number of pages7
JournalSurface and Interface Analysis
Issue number1
Publication statusPublished - 2006 Jan

All Science Journal Classification (ASJC) codes

  • General Chemistry
  • Condensed Matter Physics
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films
  • Materials Chemistry


Dive into the research topics of 'Surface characteristics of titanium-silver alloys in artificial saliva'. Together they form a unique fingerprint.

Cite this