Significant enhancement of the dielectric constant through the doping of CeO 2 into HfO 2 by atomic layer deposition

Woo Hee Kim, Min Kyu Kim, Il Kwon Oh, Wan Joo Maeng, Taehoon Cheon, Soo Hyun Kim, Atif Noori, David Thompson, Schubert Chu, Hyungjun Kim

Research output: Contribution to journalArticlepeer-review

18 Citations (Scopus)


Films of CeO2 were deposited by atomic layer deposition (ALD) using a Ce(mmp)4 [mmp = 1-methoxy-2-methyl-2-propanolate] precursor and H2O reactant. The growth characteristics and film properties of ALD CeO2 were investigated. The ALD CeO2 process produced highly pure, stoichiometric films with polycrystalline cubic phases. Using the ALD CeO2 process, the effects of Ce doping into an HfO2 gate dielectric were systematically investigated. Regardless of Ce/(Ce + Hf) composition, all ALD CexHf1-xO2 films exhibited constant growth rates of approximately 1.3 Å/cycle, which is essentially identical to the ALD HfO2 growth rates. After high-temperature vacuum annealing at 900°C, it was verified, based on X-ray diffraction and high-resolution cross-sectional transmission electron microscopy results, that all samples with various Ce/(Ce + Hf) compositions were transformed from nanocrystalline to stabilized cubic or tetragonal HfO2 phases. In addition, the dielectric constant of the CexHf1-xO 2 films significantly increased, depending on the Ce doping content. The maximum dielectric constant value was found to be nearly 39 for the Ce/(Ce + Hf) concentration of ~11%.

Original languageEnglish
Pages (from-to)1164-1169
Number of pages6
JournalJournal of the American Ceramic Society
Issue number4
Publication statusPublished - 2014 Apr

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Materials Chemistry


Dive into the research topics of 'Significant enhancement of the dielectric constant through the doping of CeO 2 into HfO 2 by atomic layer deposition'. Together they form a unique fingerprint.

Cite this