Anhydrous polymer electrolyte membranes with cross-linked structure have been prepared based on poly(vinyl alcohol-co-ethylene) (PVA-co-PE) copolymer. The PVA units of copolymer served to induce thermal cross-linking with 4,5-imidazole dicarboxylic acid (IDA) via esterification while PE units controlled the membrane swelling and the mechanical properties of films. Upon doping with phosphoric acid (PA, H3PO4) to form imidazole-PA complexes, the proton conductivity of membranes continuously increased with increasing PA content. As a result, proton conductivity reached 0.01 S/cm at 100 °C under anhydrous conditions. X-ray diffraction analysis revealed that both the d-spacing and crystalline peak of membranes were reduced upon introduction of IDA/PA due to the cross-linking effect. The PVA-co-PE/IDA/PA membranes exhibited good mechanical properties, e.g., 150 MPa of Young's modulus, as determined by a universal testing machine. Thermal gravimetric analysis also represented that the thermal stability of membranes was increased up to 200 °C upon introduction of IDA/PA.
|Number of pages||6|
|Publication status||Published - 2010 Jun|
Bibliographical noteFunding Information:
Acknowledgment This work was supported by the Korea Science and Engineering Foundation (KOSEF) grant funded by the Korea government (MEST) (R01-2008-000-10112-0) and (MOEHRD, Basic Research Promotion Fund) (KRF-2008-331-D00152).
All Science Journal Classification (ASJC) codes
- Chemical Engineering(all)
- Materials Science(all)
- Physics and Astronomy(all)