Microfabrication and mechanical properties of nanoporous gold at the nanoscale

Dongyun Lee, Xiaoding Wei, Xi Chen, Manhong Zhao, Seong C. Jun, James Hone, Erik G. Herbert, Warren C. Oliver, Jeffrey W. Kysar

Research output: Contribution to journalArticlepeer-review

131 Citations (Scopus)


The mechanical properties of nanowires consisting of nanoporous gold are studied experimentally. The nanoporous gold is synthesized from dealloyed "white gold" leaf (Au37.4 and Ag62.6 in at.%) into a free-standing dog-bone-shaped specimen with a gauge section 7 μm long, 300 nm wide, and 100 nm thick. The elastic modulus, residual stress, and yield stress are measured by deflective tensile testing and nanoindentation, and are about 9 GPa, 65 MPa, and 110 MPa, respectively.

Original languageEnglish
Pages (from-to)437-440
Number of pages4
JournalScripta Materialia
Issue number5
Publication statusPublished - 2007 Mar

Bibliographical note

Funding Information:
J.W.K. acknowledges support from NSF CMS-0134226 and AFOSR FA5550-06-1-0214. This work was also supported by the Academic Quality Fund from Columbia University and has used the shared experimental facilities supported primarily by the MRSEC Program of the National Science Foundation under Award Number DMR-0213574 and by the New York State Office of Science, Technology and Academic Research (NYSTAR) as well as the shared experimental facilities of NSEC Program of the National Science Foundation under NSF CHE-0117752. X.C. acknowledges support from NSF CMS-0407743. The authors thank Prof. J. Erlebacher and Dr. C.A. Volkert for interesting discussions.

All Science Journal Classification (ASJC) codes

  • General Materials Science
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys


Dive into the research topics of 'Microfabrication and mechanical properties of nanoporous gold at the nanoscale'. Together they form a unique fingerprint.

Cite this