Influence of cement thickness on resin-zirconia microtensile bond strength

Tae Hoon Lee, Jin Soo Ahn, June Sung Shim, Chong Hyun Han, Sun Jai Kim

Research output: Contribution to journalArticlepeer-review

12 Citations (Scopus)


Purpose: The aim of this study was to evaluate the influence of resin cement thickness on the microtensile bond strength between zirconium-oxide ceramic and resin cement. Materials and methodsP: Thirty-two freshly extracted molars were transversely sectioned at the deep dentin level and bonded to air-abraded zirconium oxide ceramic disks. The specimens were divided into 8 groups based on the experimental conditions (cement type: Rely X UniCem or Panavia F 2.0, cement thickness: 40 or 160 μm, storage: thermocycled or not). They were cut into microbeams and stored in 37°C distilled water for 24 h. Microbeams of non-thermocycled specimens were submitted to a microtensile test, whereas those of thermocycled groups were thermally cycled for 18,000 times immediately before the microtensile test. Three-way ANOVA and Sheffe's post hoc tests were used for statistical analysis (α=95%). Results: All failures occurred at the resin-zirconia interface. Thermocycled groups showed lower microtensile bond strength than non-thermocycled groups (P<.001). Differences in cement thickness did not influence the resin-zirconia microtensile bond strength given the same resin cement or storage conditions (P>.05). The number of adhesive failures increased after thermocycling in all experimental conditions. No cohesive failure was observed in any experimental group. Conclusion. When resin cements of adhesive monomers are applied over air-abraded zirconia restorations, the degree of fit does not influence the resin-zirconia microtensile bond strength.

Original languageEnglish
Pages (from-to)119-125
Number of pages7
JournalJournal of Advanced Prosthodontics
Issue number3
Publication statusPublished - 2011

All Science Journal Classification (ASJC) codes

  • Oral Surgery
  • Dentistry (miscellaneous)


Dive into the research topics of 'Influence of cement thickness on resin-zirconia microtensile bond strength'. Together they form a unique fingerprint.

Cite this