Hydrogenated Graphenes by Birch Reduction: Influence of Electron and Proton Sources on Hydrogenation Efficiency, Magnetism, and Electrochemistry

Alex Yong Sheng Eng, Zdeněk Sofer, Štěpán Huber, Daniel Bouša, Miroslav Maryško, Martin Pumera

Research output: Contribution to journalArticlepeer-review

25 Citations (Scopus)


Interest in chemical functionalisation of graphenes today is largely driven by associated changes to its physical and material properties. Functionalisation with hydrogen was employed to obtain hydrogenated graphenes (also termed graphane if fully hydrogenated), which exhibited properties including fluorescence, magnetism and a tuneable band gap. Although the classical Birch reduction has been employed for hydrogenation of graphite oxide, variation exists between the choice of alkali metals and alcohols/water as quenching agents. A systematic study of electron (Li, Na, K, Cs) and proton sources (tBuOH, iPrOH, MeOH, H2O) has been performed to identify optimal conditions. The proton source exerted a great influence on the resulting hydrogenation with water and out-performed alcohols, and the lowest carbon-to-hydrogen ratio was observed with sodium and water with composition of C1.4H1O0.3. Although ferromagnetism at room temperature correlates well with increasing hydrogen concentrations, small contributions from trace iron impurities cannot be completely eliminated. In contrast, hydrogenated graphenes exhibit a significant paramagnetic moment at low temperatures that has no correlation with impurities, and therefore, originates from the carbon system. This is in comparison to graphene, which is strongly diamagnetic, and concentrations of paramagnetic centres in hydrogenated graphenes are one order of magnitude larger than that in graphite. Nonetheless, hydrogenation over a particular level might also excessively disrupt intrinsic sp2 conjugation, resulting in unintended reduction of electrochemical properties. This was observed with heterogeneous electron-transfer rates and it was postulated that hydrogenated graphenes should generally have high defect densities, but only moderately high hydrogenation, should they be employed as electrode materials.

Original languageEnglish
Pages (from-to)16828-16838
Number of pages11
JournalChemistry - A European Journal
Issue number47
Publication statusPublished - 2015 Nov 1

Bibliographical note

Publisher Copyright:
© 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

All Science Journal Classification (ASJC) codes

  • Catalysis
  • Organic Chemistry


Dive into the research topics of 'Hydrogenated Graphenes by Birch Reduction: Influence of Electron and Proton Sources on Hydrogenation Efficiency, Magnetism, and Electrochemistry'. Together they form a unique fingerprint.

Cite this