Fabrication of a bulk icosahedral material through mechanical alloying of the powder mixture Ti41.5Zr41.5Ni17

S. Yi, K. B. Kim, E. Fleury, W. T. Kim, D. H. Kim

Research output: Contribution to journalArticlepeer-review

17 Citations (Scopus)


A bulk material that consists of the stable icosahedral phases (I-phases) in the Ti-Zr-Ni system has been fabricated in a hot press using mechanically alloyed (MA) powders. Considerable amounts of amorphous phase and nanocrystals are formed after MA for more than 30 h in the mixture of elemental powders (Ti, Zr, Ni) with the overall composition of Ti41.5Zr41.5Ni17. The amorphous phase transforms into the I-phase in the temperature range of 573-673 K during continuous heating in differential scanning calorimetry (DSC) with the heating rate of 40 K/min. The powders MA for 40 h are hot-pressed for 2 h at 873 K under the applied pressure of 900 MPa to form a bulk I-phase material. The evolution of the Vickers microhardness has been examined in the load range of 0.5-10 N. The indentation size effect is accompanied by a modification of the fracture pattern. At a low value of the load, no crack is observed. As the load increases, the first cracks observed around the indenter are lateral cracks, and then radial cracks are found for load larger than 1 N.

Original languageEnglish
Pages (from-to)75-79
Number of pages5
JournalMaterials Letters
Issue number1-2
Publication statusPublished - 2002 Jan

Bibliographical note

Funding Information:
This work was supported by the Creative Research Initiatives of the Korean Ministry of Science and Technology.

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering


Dive into the research topics of 'Fabrication of a bulk icosahedral material through mechanical alloying of the powder mixture Ti41.5Zr41.5Ni17'. Together they form a unique fingerprint.

Cite this