Epigallocatechin-3-O -gallate-loaded poly(lactic-co-glycolic acid) fibrous sheets as anti-adhesion barriers

Jong Ho Lee, Yong Cheol Shin, Won Jun Yang, Jong Chul Park, Suong Hyu Hyon, Dong Wook Han

Research output: Contribution to journalArticlepeer-review

18 Citations (Scopus)


Epigallocatechin-3-O -gallate (EGCG), the main polyphenolic component of green tea, has a wide range of pharmacological activities, including antioxidant, anti-inflammatory, and anti-fibrotic effects. In this study, EGCG-loaded poly(lactic-coglycolic acid) (PLGA) sheets were prepared by electrospinning nanofibers and evaluating their potential as tissue-adhesion barriers. EGCG-loaded PLGA (E-PLGA) fibrous sheets were electrospun from a PLGA solution containing 8% (w/v) EGCG. The average diameter of E-PLGA fibers was 397 ± 159 nm, which was comparable to that of pure PLGA fibers (459 ± 154 nm). EGCG was uniformly dispersed in E-PLGA sheets without direct chemical interactions. E-PLGA fibrous sheets showed sustained release of EGCG by controlled diffusion and PLGA degradation. The attachment and proliferation of L-929 fibroblastic cells were significantly (p < 0.05) suppressed in E-PLGA sheets. Furthermore, E-PLGA fibrous sheets did not induce any inflammatory response to J774A.1 macrophages. The anti-adhesion efficacy of E-PLGA fibrous sheets was evaluated in the intraperitoneal adhesion model in rats. Two weeks after surgical treatment, macroscopic adhesion (extent and severity) scores and histopathological tissue responses of E-PLGA fibrous sheets were significantly lower than those of non-treated controls and pure PLGA sheets. The results suggest that the scores are comparable, and in some cases superior, to those of other commercialized tissue-adhesion barriers. In conclusion, our study findings suggest that E-PLGA fibrous sheets may be exploited as potential tissue-adhesion barriers for the prevention of post-surgical adhesion formation.

Original languageEnglish
Pages (from-to)1461-1471
Number of pages11
JournalJournal of Biomedical Nanotechnology
Issue number8
Publication statusPublished - 2014 Aug 1

Bibliographical note

Publisher Copyright:
© 2015 American Scientific Publishers.

All Science Journal Classification (ASJC) codes

  • Bioengineering
  • Medicine (miscellaneous)
  • Biomedical Engineering
  • Materials Science(all)
  • Pharmaceutical Science


Dive into the research topics of 'Epigallocatechin-3-O -gallate-loaded poly(lactic-co-glycolic acid) fibrous sheets as anti-adhesion barriers'. Together they form a unique fingerprint.

Cite this