Effect of phonon confinement on the thermal conductivity of In0.53Ga0.47As nanofilms

Jungwon Kim, Hoon Kim, Mehmet Emin Kilic, Chhatrasal Gayner, Rachel Koltun, Hwanjoo Park, Aloysius Soon, John Bowers, Chris Palmstrøm, Woochul Kim

Research output: Contribution to journalArticlepeer-review

6 Citations (Scopus)


Over the past few decades, significant progress has been made to manipulate thermal transport in solids. Most of the effort has focused on reducing the phonon mean free path through boundary scattering. Herein, we demonstrate that the phonon confinement effect can also be used as a tool for managing thermal transport in solids. We measured the thermal conductivities of 10-70-nm-thick In0.53Ga0.47As nanofilms and found that the thermal conductivities decrease as the film thickness decreases. However, the reasons for this reduction differ for films with different thicknesses. The thermal conductivity of the 30- and 70-nm-thick In0.53Ga0.47As nanofilms decreases because of severe phonon boundary scattering. Our analysis indicates that phonon confinement occurs in the 10- and 20-nm-thick In0.53Ga0.47As nanofilms, which modifies phonon dispersion leading to changes in the phonon group velocity and the Debye temperature. These experimental and theoretical results could help to elucidate the phonon confinement effect in nanomaterials as well as establish a platform for understanding nanoscale thermal physics.

Original languageEnglish
Article number245103
JournalJournal of Applied Physics
Issue number24
Publication statusPublished - 2018 Jun 28

Bibliographical note

Funding Information:
This research was supported by the Nano-Material Technology Development Program (Green Nano Technology Development Program; 2011-0030146) through a National Research Foundation of Korea Grant funded by the Ministry of Education, Science and Technology.

Publisher Copyright:
© 2018 Author(s).

All Science Journal Classification (ASJC) codes

  • Physics and Astronomy(all)


Dive into the research topics of 'Effect of phonon confinement on the thermal conductivity of In0.53Ga0.47As nanofilms'. Together they form a unique fingerprint.

Cite this