Effect of Mg(OH)2/silica composite aerogel filler on the glass transition temperature and flame retardancy of detachable polymer coatings

Kyu Yeon Lee, Varsha D. Phadtare, Vinayak G. Parale, Younghun Kim, Hyung Ho Park

Research output: Contribution to journalArticlepeer-review

3 Citations (Scopus)

Abstract

Polymer-based detachable coatings are used to protect industrial products and military equipment from surface damage and contamination during manufacturing and transportation. To expand their application to various industrial fields, it is essential to simultaneously implement diverse characteristics, such as low glass transition temperature, high detachability and uniformity, and high flame retardancy. In this study, we prepared Mg(OH)2/silica composite aerogel, which was used to prepare a detachable poly(vinyl butyral) coating solution to improve the flame retardancy and reduce the glass transition temperature of the coating. Furthermore, we investigated the effect of the addition of a surfactant for achieving a detachable coating with good uniformity and flame retardancy. The coating prepared using the Mg(OH)2/silica composite aerogel and nonionic surfactant exhibited a surface area of 496 m2/g. In addition, the coating maintained its flexibility even at sub-zero temperature (−7 °C) and exhibited significantly improved flame retardancy as it withstood fire for more than 15 s before igniting compared to the original coating.

Original languageEnglish
Article number107050
JournalProgress in Organic Coatings
Volume171
DOIs
Publication statusPublished - 2022 Oct

Bibliographical note

Publisher Copyright:
© 2022 Elsevier B.V.

All Science Journal Classification (ASJC) codes

  • General Chemical Engineering
  • Surfaces, Coatings and Films
  • Organic Chemistry
  • Materials Chemistry

Fingerprint

Dive into the research topics of 'Effect of Mg(OH)2/silica composite aerogel filler on the glass transition temperature and flame retardancy of detachable polymer coatings'. Together they form a unique fingerprint.

Cite this