T1 - Effect of grain boundary serration on the tensile properties of the super 304H heat resistant austenitic stainless steel
AU - Hong, Sung Min
AU - Min, Dong Joon
AU - Fleury, Eric
PY - 2010
Y1 - 2010
N2 - Grain boundary serrations were produced in heat-resistant austenitic stainless steel containing Cu by applying after solution heat-treatment a holding time in the range 700-800°C between 30 minutes to 3 hours. These special treatments provide an enhancement of the tensile ductility of about 40 and 113%at room temperature and 750°C, respectively, while no significant change in the yield stress and tensile strength could be observed.
AB - Grain boundary serrations were produced in heat-resistant austenitic stainless steel containing Cu by applying after solution heat-treatment a holding time in the range 700-800°C between 30 minutes to 3 hours. These special treatments provide an enhancement of the tensile ductility of about 40 and 113%at room temperature and 750°C, respectively, while no significant change in the yield stress and tensile strength could be observed.
KW - Ductility
KW - Grain boundary serration
KW - Heat-resistant austenitic stainless steel
KW - Heat-treatment
UR - https://www.scopus.com/pages/publications/77955495464
UR - https://www.scopus.com/pages/publications/77955495464#tab=citedBy
U2 - 10.4028/www.scientific.net/MSF.654-656.170
DO - 10.4028/www.scientific.net/MSF.654-656.170
M3 - Conference contribution
AN - SCOPUS:77955495464
SN - 0878492550
SN - 9780878492558
T3 - Materials Science Forum
SP - 170
EP - 173
BT - PRICM7
PB - Trans Tech Publications Ltd
T2 - 7th Pacific Rim International Conference on Advanced Materials and Processing, PRICM-7
Y2 - 2 August 2010 through 6 August 2010
ER -