Abstract
The average diffusion coefficient D of polymer chains across particle interfaces having different surface functionality was obtained from dynamic mechanical analysis to compare the results of the rate of tensile strength development. The rate of tensile strength development was decreased with increasing surface functionality of reactive latexes. This indicated that the interpaticular crosslinking reaction restricted the interdiffusion of polymer chains during film formation and annealing process.
Original language | English |
---|---|
Pages (from-to) | 298-304 |
Number of pages | 7 |
Journal | Journal of Industrial and Engineering Chemistry |
Volume | 3 |
Issue number | 4 |
Publication status | Published - 1997 |