Control of Si3N4 etching kinetics and selectivity to SiO2 by the additives in superheated water

Changjin Son, Sangwoo Lim

Research output: Contribution to journalArticlepeer-review

10 Citations (Scopus)


Selective etching of Si3N4 to SiO2 is essential in the semiconductor fabrication process. In particular, as the number of alternating Si3N4/SiO2 multi-layered stacks increases, selective removal of Si3N4 without loss of SiO2 becomes difficult. In this study, the dissolution of Si3N4 was demonstrated in superheated water without addition of H3PO4, which has been widely used to etch Si3N4. The dissolution rates of Si3N4 and SiO2 in the superheated water depended strongly on the concentration of OH, and the activation energy obtained for the dissolution of Si3N4 was 72.65 ± 0.95 kJ/mol. It is believed that the attack of the partially δ+ charged Si atoms in the Si3N4 by nucleophilic OH was the key step in the dissolution of Si3N4 in the superheated water. Because a tradeoff between the dissolution rate of Si3N4 and the Si3N4-to-SiO2 etching selectivity was observed, H2SiO3 and HF were added to HCl-based superheated water for optimization. The HCl-based superheated water with the addition of 0.005 vol% HF and 0.01 M H2SiO3 allowed successful fabrication of a horizontal SiO2 trench structure on a patterned Si3N4/SiO2 15 pair-layered stack through selective etching of Si3N4 without thinning of the SiO2 layer.

Original languageEnglish
Pages (from-to)N85-N91
JournalECS Journal of Solid State Science and Technology
Issue number4
Publication statusPublished - 2019

Bibliographical note

Funding Information:
This research was supported by the Ministry of Trade, Industry & Energy (10080628) and Korea Semiconductor Research Consortium Support Program for the development of the future semiconductor device.

Publisher Copyright:
© The Author(s) 2019.

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials


Dive into the research topics of 'Control of Si3N4 etching kinetics and selectivity to SiO2 by the additives in superheated water'. Together they form a unique fingerprint.

Cite this