Cationic effect of charge compensation on the sulfide capacity of aluminosilicate slags

Joon Sung Choi, Youngjoo Park, Sunghee Lee, Dong Joon Min

Research output: Contribution to journalArticlepeer-review

11 Citations (Scopus)


The effect of CaO on the sulfide capacity of CaO-Al2O3-SiO2 slags was studied from the viewpoint of the ionic structure of alumina in slag. The aluminum coordination number was analyzed using 27Al 500-MHz solid nuclear magnetic resonance spectroscopy and the results were compared with those of the sulfide capacity analysis. The sulfide capacity of slag, in the peralkaline region (XCaO/XAl2O3 > 1.0), exhibited a linear relationship with respect to basicity (ao2-) as excess free Ca2+ formed a 4-coordinated aluminum unit structure ([IV]Al; AlO5-4) and stabilized the sulfide ions (γS2-). However, sulfide capacity in the peraluminous region (XCaO/XAl2O3 < 1.0) exhibited a nonlinear relationship with respect to basicity (ao2-) owing to the structure of higher-coordinated aluminum units ([V]Al, [VI]Al; Al3+) and the relative lack of Ca2+. Therefore, the sulfide capacity of high Al2O3-bearing slags strongly depended on the basicity (aO2-) and stability of sulfide ions (γS2-), which depended on the competitive behavior of Ca2+ owing to the structural changes in Al2O3. The effect of the aluminum coordination number on the sulfide capacity was discussed in detail using an analysis of the slag structure and thermodynamics model.

Original languageEnglish
Pages (from-to)2856-2867
Number of pages12
JournalJournal of the American Ceramic Society
Issue number7
Publication statusPublished - 2018 Jul

Bibliographical note

Funding Information:
This work was supported by the Ministry of Trade, Industry and Energy under Project No. 10063488. This work was supported by the third stage of Brain Korea 21 Plus Project in Division of Creative Materials.

Publisher Copyright:
© 2018 The American Ceramic Society

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Materials Chemistry


Dive into the research topics of 'Cationic effect of charge compensation on the sulfide capacity of aluminosilicate slags'. Together they form a unique fingerprint.

Cite this