Annealing effects on the properties of HfO2 films grown by metalorganic molecular beam epitaxy

Tae Hyoung Moon, Jae Woong Lee, Moon Ho Ham, Jae Min Myoung

Research output: Contribution to journalArticlepeer-review

13 Citations (Scopus)


We present the annealing effects on the properties of HfO2 dielectrics grown by metalorganic molecular beam epitaxy. From the comparison of the line shapes of core-level spectra for the N2-annealed samples with different annealing temperatures, the concentrations of SiO and Hf-silicate with high dielectric constant are found to be highest for HfO2 film annealed at 700 °C. Therefore, this result supports that the accumulation capacitance of the sample annealed at 700 °C in N2 ambient is not deteriorated in spite of the steep increase of interfacial layer thickness. For the O2-annealed samples, SiO2 with low dielectric constant is widely spread throughout the samples as the annealing temperature increases. Therefore, the accumulation capacitance density is degraded due to the increase in the thickness of the interfacial layer which mainly consists of SiO2.

Original languageEnglish
Pages (from-to)2452-2457
Number of pages6
JournalMicroelectronic Engineering
Issue number11-12
Publication statusPublished - 2006 Nov

Bibliographical note

Funding Information:
This research was supported by the Ministry of Information and Communication (MIC), Korea, under the Information Technology Research Center (ITRC) support program supervised by the Institute of Information Technology Assessment (IITA).

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Atomic and Molecular Physics, and Optics
  • Condensed Matter Physics
  • Surfaces, Coatings and Films
  • Electrical and Electronic Engineering


Dive into the research topics of 'Annealing effects on the properties of HfO2 films grown by metalorganic molecular beam epitaxy'. Together they form a unique fingerprint.

Cite this