A novel porous scaffold designed for application as a bone substitute, with a structure containing three-dimensional (3D) pore channels in a hydroxyapatite (HA) scaffold, was fabricated using a combination of a solid freeform fabrication (SFF) and cast in a mold using freezing casting method. This study was performed to evaluate the physical and biomechanical properties of the HA scaffolds fabricated by SFF and using polymer replication method (PRM), one of the conventional methods. Although the phase composition and porosity of these two scaffolds are similar, their external shape and mechanical property were different. All of the fabricated scaffolds showed similar patterns through X-ray diffraction. The difference between porosities of two HA scaffolds were not statistically significant (P>0.05). However, the average compressive strength of the scaffold fabricated by SFF was 14.6 MPa, and that of the scaffold fabricated using polymer replication was 3.56MPa (P<0.05). It was confirmed that SFF fabrication could have a relatively higher mechanical property than PRM fabrication at the same porosity.
|Number of pages
|International Journal of Precision Engineering and Manufacturing
|Published - 2011 Aug
Bibliographical noteFunding Information:
This study was supported by a grant of the Korea Healthcare technology R&D Project, Ministry for Health & Welfare, Republic of Korea (A091167).
All Science Journal Classification (ASJC) codes
- Mechanical Engineering
- Industrial and Manufacturing Engineering
- Electrical and Electronic Engineering